Double coated tapes with low outgas. Excellent damper effect.
-
- Product name
- T4412W
-
- Features
-
- Adhesive helps to suppress vibration.
- Low out gassing.
- Highly adhesive to SUS, aluminum and plastic materials.
Safety Data Sheet (SDS) Download
Related articles
Structure
Specifications
| Product name | T4412W *2 |
|---|---|
| Main component | Acrylic base |
| Carrier | Non-carrier |
| Color | Transparent |
| Adhesive thickness(µm) | About 45 |
| Release film thickness (µm) | About 50+38 |
| Bonding strength(N/20mm) *1 | 12 |
| St'd size(width & length) | 500mm x 100m |
| Warranty period from manufacturing date | 12 months |
- *1180° peeling strength
- *2With both side release film
Ideal for bonding metal dampers and foam insulators in HDD due to low out gassing characteristics.
1.Bonding strength on various type of substrate (180° peeling)
Test Piece condition
Tape width:20mm
Bonding condition:One stroke with 2-kg roller
Measuring condition:23°C±5°C 60%±20%RH
Peeling speed:300mm/min
Backing material:25µm PET
[Left at RT for one hour before measurement]
Results
(N/20mm)
| 180° peeling strength | Product name | Substrate | |
|---|---|---|---|
| SUS | PI | ||
| T4412W | 12 | 11 | |
2.Bonding strength at different temperatures (180° peeling)
Test Piece condition
Substrate:Stainless steel plate (SUS304)Tape width:20mm
Bonding condition:One stroke with 2-kg roller
Measuring condition:23°C±5°C 60%±20%RH
Peeling speed:300mm/min
Backing material:25µm PET
[Left at RT for one hour and then at each temperature for 30 minutes before measurement]
| 180° peeling strength | Product name | Measurement temperature | |||
|---|---|---|---|---|---|
| 23°C | 40°C | 60°C | 80°C | ||
| T4412W | 12 | 11 | 10 | 8 | |
Test Piece condition
Substrate:Stainless steel plate (SUS304)
Bonding area:25mm x 25mm
Bonding condition:One stroke with 2-kg roller
Backing material:25µm PET
[Left at RT for one hour and then at each temperature for 30 minutes before measurement]
[Creep length after one hour application of 1-kg load]
Results
| Creep length(mm) | Product name | Measuring temperature | |
|---|---|---|---|
| 40°C | 100°C | ||
| T4412W | 0.2 | 0.3 | |
4.Outgas
Test Piece condition
Test method:Dynamic headspace method (Purge & Trap) Gas chromatography-mass spectrometry. (Desorption and purge : 250°C 15min, He 100ml/min, Trap : -60°C, Tenax TA)
Outgassing condition:120°C 1hour
Standard substance:Tetra-decane
Results
| Outgas (ppm) | Product name | Tetra-decane conversion |
|---|---|---|
| T4412W | 90 |
caution
Note on the characteristic data given - Data on the characteristics of the products described in this page based on the results of evaluations carried out by the company. This does not guarantee that the characteristics of the product conform with your usage environment. Before use, review the usage conditions based on evaluation data obtained from the equipment and substrates actually used.